Abstract The aim of this study was to evaluate the influence of adding quaternary ammonium methacrylates (QAMs) to experimental adhesives by assessing the degree of conversion (DC), cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. Two QAMs were added to an experimental adhesive: dimethylaminododecyl methacrylate bromododecane (DMADDM) or dimethylaminododecyl methacrylate bromohexadecane (DMAHDM) at three concentrations each: 1, 2.5, and 5 wt.%. Experimental adhesive without QAMs (control group) and commercially available Transbond XT Primer (3M Unitek, Monrovia, California, USA) were used for comparisons. The adhesives were tested for DC, cytotoxicity against keratinocytes and fibroblasts, and antibacterial activity against biofilm formation. DC, cytotoxicity against fibroblasts, and antibacterial activity were analyzed using one-way ANOVA and Tukey’s multiple comparisons. Cytotoxicity against keratinocytes was evaluated using the Kruskal Wallis and Dunn’s post-hoc (α = 5%) tests. Transbond showed lower DC as compared to 5% DMAHDM, 1% DMADDM, and 5% DMADDM (p < 0.05). However, all groups presented proper DC when compared to commercial adhesives in the literature. In the evaluation of cytotoxicity against keratinocytes, Transbond induced higher viability than 2.5 wt.% groups (p < 0.05). Against fibroblasts, Transbond induced higher viability as compared to 5 wt.% groups (p < 0.05). DMAHDM at 5 wt.% reduced biofilm formation when compared to all the other groups (p < 0.05). Despite their cytotoxic effect against keratinocytes, gingival fibroblasts showed higher viability. DMAHDM at 5 wt.% decreased Streptococcus mutans viability. The incorporation of DMAHDM at 5 wt.% may be a strategy for reducing the development of white spot lesions.

O estudo buscou avaliar as compras de resina composta em um sistema público de saúde e compreender as variáveis associadas com o custo e o processo decisório ao longo dos últimos dez anos. Os dados secundários foram coletados do Banco de Preços em Saúde (BPS), do governo federal, entre 2010 e 2019. Foram selecionadas todas as resinas compostas convencionais e bulk-fill. Os seguintes dados foram coletados: data de compra, tipo e localização da instituição, modalidade de licitação, número de itens comprados, fabricante e preços unitários. Um modelo de regressão linear múltipla avaliou o impacto do preço nas variáveis de licitação, enquanto a regressão logística variada comparou as probabilidades de compra entre os materiais. Foram coletadas 18.138 observações com 2.129.294 unidades compradas e um custo total de USD 43.504.260,00. As resinas convencionais apareceram em 98,5% dos processos de licitação. As resinas convencionais nanofilled foram os materiais mais comprados, com um aumento na probabilidade de compra ao longo do tempo, apesar dos preços mais elevados. Foi previsto um aumento nos preços de materiais bulk-fill em comparação com os convencionais. A probabilidade de compra dessa categoria aumentou em 3,14 vezes por ano. Variáveis sociodemográficas e educacionais influenciam os preços e a probabilidade de compra no sistema de saúde. As resinas nanofilled e bulk-fill são incluídas cada vez mais na prática clínica. Os achados destacam possíveis modificações no padrão de tratamentos de restauração e na maneira que a translação de conhecimento pode ocorrer, desde o desenvolvimento de materiais novos até a aplicação clínica, à luz do impacto econômico dessas modificações.

This study aims to assess the resin composite purchases in a public health system and understand the variables associated with its cost and with the decision-making process over a period of 10 years. Secondary data collection was performed using the Brazilian Healthcare Prices Database (BDHP) from 2010 to 2019. All conventional and bulk-fill composites were selected. Date of purchase, institution type and location, procurement modality, number of purchased items, manufacture, and unit prices were collected. A multiple linear regression model assessed the influence of price in the procurement variables, while a multinomial logistic regression compared purchase probabilities between the materials. In total, 18,138 observations were collected with 2,129,294 purchased units and a total cost of USD 43,504,260.00. Conventional composites appeared in 98.5% of the procurement process. Nanofilled conventional composites were the most purchased materials, with an increased probability of purchase over time, despite its higher prices. An increase in prices was predicted for bulk-fill materials when compared to conventional ones. The odds of purchasing this category increased by 3.14x for every price increase over the years. Sociodemographic and type of institution influences the prices and the probability of procurement in the healthcare system. Nanofilled and bulk-fill resin are increasingly included in clinical practice. These findings highlight possible modifications to the standard-of-care in restorative treatments and how the translation of knowledge may occur from the development of new materials to the clinical application considering the economic impact of these modifications.

El objetivo de este estudio fue evaluar las adquisiciones de resina compuesta en un sistema público de salud y comprender las variables asociadas con el coste y proceso de toma de decisión a lo largo de los últimos diez años. Se realizó una recogida de datos en el Banco de Datos de Precios de Atención Sanitaria (BDHP), de Brasil, de 2010 a 2019. Se seleccionaron todas las resinas convencionales y bulk-fill. Se recogieron: fecha de compra, tipo de institución y localización, modalidad de adquisición, número de ítems comprados, manufactura, y precios unitarios. Un modelo de regresión lineal múltiple evaluó la influencia del precio en las variables de adquisición, mientras una regresión multinomial logística comparó las probabilidades de compra entre los materiales. Se recogieron 18.138 observaciones con 2.129.294 unidades adquiridas y un coste total de USD 43.504.260,00. Las resinas convencionales aparecieron en un 98,5% del proceso de adquisición. Las resinas convencionales de nanorelleno fueron los materiales más comúnmente comprados, con una probabilidad mayor de compra a lo largo del tiempo, pese a sus precios más altos. Se predijo un aumento de los precios en los materiales bulk-fill, cuando se compararon con los convencionales. La probabilidad de compra en esta categoría se incrementa un 3,14x por cada aumento durante el año. Las variables sociodemográficas y educacionales influencian los precios y la probabilidad de adquisición en el sistema de salud público. Las resinas de nanorelleno y bulk-fill están incluidas cada vez más en la práctica clínica. Estos resultados subrayan las posibles modificaciones en el estándar de cuidado de los tratamientos restaurativos, y cómo se produce la transferencia de conocimientos, desde el desarrollo de nuevos materiales hasta su aplicación clínica, a la luz del impacto económico de estas modificaciones.

O estudo buscou avaliar as compras de resina composta em um sistema público de saúde e compreender as variáveis associadas com o custo e o processo decisório ao longo dos últimos dez anos. Os dados secundários foram coletados do Banco de Preços em Saúde (BPS), do governo federal, entre 2010 e 2019. Foram selecionadas todas as resinas compostas convencionais e bulk-fill. Os seguintes dados foram coletados: data de compra, tipo e localização da instituição, modalidade de licitação, número de itens comprados, fabricante e preços unitários. Um modelo de regressão linear múltipla avaliou o impacto do preço nas variáveis de licitação, enquanto a regressão logística variada comparou as probabilidades de compra entre os materiais. Foram coletadas 18.138 observações com 2.129.294 unidades compradas e um custo total de USD 43.504.260,00. As resinas convencionais apareceram em 98,5% dos processos de licitação. As resinas convencionais nanofilled foram os materiais mais comprados, com um aumento na probabilidade de compra ao longo do tempo, apesar dos preços mais elevados. Foi previsto um aumento nos preços de materiais bulk-fill em comparação com os convencionais. A probabilidade de compra dessa categoria aumentou em 3,14 vezes por ano. Variáveis sociodemográficas e educacionais influenciam os preços e a probabilidade de compra no sistema de saúde. As resinas nanofilled e bulk-fill são incluídas cada vez mais na prática clínica. Os achados destacam possíveis modificações no padrão de tratamentos de restauração e na maneira que a translação de conhecimento pode ocorrer, desde o desenvolvimento de materiais novos até a aplicação clínica, à luz do impacto econômico dessas modificações.

This study aims to assess the resin composite purchases in a public health system and understand the variables associated with its cost and with the decision-making process over a period of 10 years. Secondary data collection was performed using the Brazilian Healthcare Prices Database (BDHP) from 2010 to 2019. All conventional and bulk-fill composites were selected. Date of purchase, institution type and location, procurement modality, number of purchased items, manufacture, and unit prices were collected. A multiple linear regression model assessed the influence of price in the procurement variables, while a multinomial logistic regression compared purchase probabilities between the materials. In total, 18,138 observations were collected with 2,129,294 purchased units and a total cost of USD 43,504,260.00. Conventional composites appeared in 98.5% of the procurement process. Nanofilled conventional composites were the most purchased materials, with an increased probability of purchase over time, despite its higher prices. An increase in prices was predicted for bulk-fill materials when compared to conventional ones. The odds of purchasing this category increased by 3.14x for every price increase over the years. Sociodemographic and type of institution influences the prices and the probability of procurement in the healthcare system. Nanofilled and bulk-fill resin are increasingly included in clinical practice. These findings highlight possible modifications to the standard-of-care in restorative treatments and how the translation of knowledge may occur from the development of new materials to the clinical application considering the economic impact of these modifications.

El objetivo de este estudio fue evaluar las adquisiciones de resina compuesta en un sistema público de salud y comprender las variables asociadas con el coste y proceso de toma de decisión a lo largo de los últimos diez años. Se realizó una recogida de datos en el Banco de Datos de Precios de Atención Sanitaria (BDHP), de Brasil, de 2010 a 2019. Se seleccionaron todas las resinas convencionales y bulk-fill. Se recogieron: fecha de compra, tipo de institución y localización, modalidad de adquisición, número de ítems comprados, manufactura, y precios unitarios. Un modelo de regresión lineal múltiple evaluó la influencia del precio en las variables de adquisición, mientras una regresión multinomial logística comparó las probabilidades de compra entre los materiales. Se recogieron 18.138 observaciones con 2.129.294 unidades adquiridas y un coste total de USD 43.504.260,00. Las resinas convencionales aparecieron en un 98,5% del proceso de adquisición. Las resinas convencionales de nanorelleno fueron los materiales más comúnmente comprados, con una probabilidad mayor de compra a lo largo del tiempo, pese a sus precios más altos. Se predijo un aumento de los precios en los materiales bulk-fill, cuando se compararon con los convencionales. La probabilidad de compra en esta categoría se incrementa un 3,14x por cada aumento durante el año. Las variables sociodemográficas y educacionales influencian los precios y la probabilidad de adquisición en el sistema de salud público. Las resinas de nanorelleno y bulk-fill están incluidas cada vez más en la práctica clínica. Estos resultados subrayan las posibles modificaciones en el estándar de cuidado de los tratamientos restaurativos, y cómo se produce la transferencia de conocimientos, desde el desarrollo de nuevos materiales hasta su aplicación clínica, a la luz del impacto económico de estas modificaciones.

Resumo O objetivo deste estudo foi avaliar a biocompatibilidade de cimentos endodônticos experimentais à base de metacrilato contendo fosfato α-tricálcico ou hidroxiapatita nanoestruturada in vitro e in vivo. Cimentos experimentais de cura dual à base de metacrilato com a adição de fosfato de α-tricálcico (α-TCP) ou hidroxiapatita (HAp), a 10% em peso, foram formulados e comparados com AH Plus (AHP). Viabilidade celular foi avaliada por brometo de 3- (4,5-dimetil-tiazoil) -2,5-difenil-tetrazólio (MTT) e sulforodamina B (SRB). Cimentos foram implantados no tecido subcutâneo dos ratos e avaliados histologicamente. Bioatividade foi avaliada pela atividade da enzima fosfatase alcalina (ALP) e Alizarin Red (AR) utilizando células da papila apical (SCAPs) e pela deposição óssea, medida em cavidades cirúrgicas no fêmur de ratos preenchidos com AH Plus e α-TCP. Nos dois ensaios de viabilidade, HAp e AHP não apresentaram diferenças estatísticas, α-TCP apresentou menores resultados de viabilidade para o ensaio MTT (p <0,05). Resultados histológicos mostraram que houve uma diminuição do conteúdo inflamatório de acordo com os períodos, e o AHP foi o único grupo que apresentou células gigantes (período de 7 dias). A condensação das fibras colágenas aumentou conforme os períodos, sem diferenças entre os grupos. Houve aumento da atividade da ALP e deposição de nódulos mineralizados de acordo com os períodos. HAp e α-TCP apresentaram maiores valores para a atividade de ALP em 5 dias e em 5, 10 e 15 dias para AR, com diferença para o AHP (p <0,05). O α-TCP apresentou valores superiores aos 10 e 15 dias quando comparado ao HAp e AHP para AR (p <0,05). Aos 90 dias, α-TCP e controle (cavidade vazia) apresentaram maior deposição de tecido ósseo quando comparado ao AHP (p <0,05). α-TCP e HAp, presentes nos cimentos à base de metacrilato, apresentaram biocompatibilidade e potencial para serem utilizados como seladores endodônticos na prática clínica. Investigações adicionais são necessárias para obter informações sobre as propriedades físico-químicas dessas formulações de cimentos antes de sua implementação clínica.

Abstract This study aimed to evaluate, in vitro and in vivo, the biocompatibility of experimental methacrylate-based endodontic sealers containing α-tricalcium phosphate (α-TCP) or nanostructured hydroxyapatite (HAp). Experimental methacrylate-based dual-cure sealers with the addition of α-TCP or HAp, at 10%wt were formulated and compared to AH Plus (AHP). Cell viability was assessed by 3-(4,5-dimethyl-thiazoyl)-2,5-diphenyl-tetrazolium bromide (MTT), and sulforhodamine B (SRB). Sealers were implanted in rats’ subcutaneous tissue and histologically evaluated. Bioactivity was assessed by alkaline phosphatase enzyme activity (ALP) and Alizarin Red (AR), using apical papillary cells (SCAPs), and by the bone deposition measured in surgical cavities on rats’ femur filled with AH Plus or α-TCP. In both viability assays, HAp and AHP sealers were similar, and α-TCP presented lower viability compared to the others at MTT assay (p<0.05). A gradual decrease of the inflammatory response according to the periods was observed and AHP was the only that presented giant cells (7-day period). Collagen fibers condensation increased according to the periods, with no differences among sealers. There was an increase at ALP activity and mineralized nodules deposition according to periods. HAp and α-TCP presented higher values for ALP activity at 5 days and at 5, 10, and 15 days for AR and were different from AHP (p<0.05). α-TCP presented superior values at 10 and 15 days compared to HAp and AHP for AR (p<0.05). At 90 days, α-TCP and control (empty cavity) showed high bone deposition compared to AHP (p<0.05). α-TCP and HAp, in a methacrylate-based sealer, presented biocompatibility and bioactivity, with the potential to be used as endodontic sealers in clinical practice. Further investigations are required to gain information on the physicochemical properties of these sealers formulation before its clinical implementation.

Abstract Fixed orthodontic appliances may lead to biofilm accumulation around them that may increase caries risk. This study aimed to evaluate the influence of quaternary ammonium methacrylates (QAMs) on the physicochemical properties, cytotoxicity, and antibacterial activity of adhesive resins for orthodontic purposes. Methodology: A base resin was prepared with a comonomer blend and photoinitiator/co-initiator system. Two different QAMs were added to the base adhesive: dimethylaminododecyl methacrylate at 5 wt.% (DMADDM) or dimethylaminohexadecyl methacrylate (DMAHDM) at 10 wt.%. The base adhesive, without QAMs, (GC) and the commercial Transbond™ XT Primer 3M (GT) were used as control. The resins were tested immediately and after six months of aging in the water regarding the antibacterial activity and shear bond strength (SBS). The antibacterial activity was tested against Streptococcus mutans via metabolic activity assay (MTT test). The groups were also tested for the degree of conversion (DC) and cytotoxicity against keratinocytes. Results: The resins containing QAM showed antibacterial activity compared to the commercial material by immediately reducing the metabolic activity by about 60%. However, the antibacterial activity decreased after aging (p<0.05). None of the groups presented any differences for SBS (p>0.05) and DC (p>0.05). The incorporation of DMADDM and DMAHDM significantly reduced the keratinocyte viability compared to the GT and GC groups (p<0.05). Conclusion: Both adhesives with QAMs showed a significant reduction in bacterial metabolic activity, but this effect decreased after water aging. Lower cell viability was observed for the group with the longer alkyl chain-QAM, without significant differences for the bonding ability and degree of conversion. The addition of QAMs in adhesives may affect the keratinocytes viability, and the aging effects maybe decrease the bacterial activity of QAM-doped materials.

RESUMO Objetivo: Avaliar a influência da imersão em diferentes soluções desinfetantes na microdureza e rugosidade de uma resina acrílica de termoativação. Métodos: Corpos de prova de resina acrílica termopolimerizável foram imersos em água destilada, vinagre comercial de uso doméstico, hipoclorito de sódio e peróxido de hidrogênio, por períodos de 150 h ou 300 h (n=10). A microdureza Knoop e a rugosidade superficial dos corpos de prova foram avaliadas com o uso de microduro?metro e rugosímetro, respectivamente. Os dadosforam analisados com o teste análise de variância a dois critérios e Holm-Sidak, com nível de significância de 5%. Resultados: Osvalores de microdureza variaram de 16,90 ± 0,33 a 17,80 ± 0,51 e a rugosidade, de 0,05 ± 0,01a 0,08 ± 0,02. Não houve diferença nos resultados de microdureza e rugosidade entre os grupos e tempos (p>0.05). Conclusão: Dentro das limitações do estudo, é possível concluir que a utilização de vinagre ou de peróxido de hidrogênio, como alternativas para a desinfecção de resina acrílica, não provocam efeitos deletérios na dureza e no polimento da resina acrílica termoativada utilizada para confecção de próteses, nem a médio nem a longo prazo.

ABSTRACT Objective: The aim of the present study was to evaluate the influence, of immersion in different disinfectant solutions, on microhardness and surface roughness of a heat-cured acrylic resin. Methods: Specimens were immersed in distilled water, commercial vinegar for domestic use, sodium hypochlorite and hydrogen peroxide, for 150 hours or 300 hours (n=10). After periods of immersion, Knoop microhardness and surface roughness were evaluated using a microhardness tester and a roughness tester, respectively. The data were analyzed using two-way ANOVA and Holm-Sidak, at a level of significance of 5%. Results: The microhardness values ranged from 16.90 ± 0.33 to 17.80 ± 0.51 and roughness values from 0.05 ± 0.01 to 0.08 ± 0.02. There is no difference in microhardness and roughness between groups and times (p>0.05). Conclusion: Within the limitations of this study, it is possible to conclude that vinegar and hydrogen peroxide, as alternative disinfectant solutions for acrylic resin devices, did not promote deleterious effects on microhardness and polishing of a heat-cured acrylic resin used for the fabrication of prostheses, neither in the medium term nor the long term.

Abstract Methacrylamides monomers for dental applications were synthesized using a one-step procedure starting from methacrylic anhydride and the respective diamine: N,N’-(propane-1,3-diyl)-bis(N-ethyl-2-methylacrylamide) (1), N,N’-(butane-1,4-diyl)-bis(2-methacrylamide) (2), N,N’-(octane-1,8-diyl-)bis(2-methylacrylamide) (3) and N,N’-(1,4-phenylene)-bis(2-methylacrylamide) (4). The structures were confirmed by 1H NMR, 13C NMR, FTIR-ATR and UHPLC-QTOF-MS. Thermal polymerization kinetics was investigated by modulated DSC for monomers (2), (3) and (4) using heating rates of 1, 2, 3 and 5 °C min-1. All IR spectra showed the C=C axial deformation at 1610 cm-1, in 1H NMR spectra the olefinic hydrogens were observed at 5.3 an 5.8 ppm and in 13C NMR, the vinylic carbons at 120 and 140 ppm. The exact m/z values were: 267.2068, 225.1595, 281.2222 and 245.1283 for monomers (1), (2), (3) and (4), respectively. The activation energy was: -182.7; -165.8 and -156.7 kJ mol-1 for monomers (2), (3) and (4), respectively. Monomers are promising candidates for use as hydrolytic stable adhesive systems for dental applications.

Abstract The aim of this study was to evaluate the influence of polyhexamethylene guanidine hydrochloride (PHMGH) in the physico-chemical properties and antibacterial activity of an experimental resin sealant. An experimental resin sealant was formulated with 60 wt.% of bisphenol A glycol dimethacrylate and 40 wt.% of triethylene glycol dimethacrylate with a photoinitiator/co-initiator system. PHMGH was added at 0.5 (G0.5%), 1 (G1%), and 2 (G2%) wt.% and one group remained without PHMGH, used as control (GCTRL). The resin sealants were analyzed for degree of conversion (DC), Knoop hardness (KHN), and softening in solvent (ΔKHN), ultimate tensile strength (UTS), contact angle (θ) with water or α-bromonaphthalene, surface free energy (SFE), and antibacterial activity against Streptococcus mutans for biofilm formation and planktonic bacteria. There was no significant difference for DC (p > 0.05). The initial Knoop hardness ranged from 17.30 (±0.50) to 19.50 (± 0.45), with lower value for GCTRL (p < 0.05). All groups presented lower KHN after immersion in solvent (p < 0.05). The ΔKHN ranged from 47.22 (± 4.30) to 57.22 (± 5.42)%, without significant difference (p > 0.05). The UTS ranged from 54.72 (± 11.05) MPa to 60.46 (± 6.50) MPa, with lower value for G2% (p < 0.05). PHMGH groups presented no significant difference compared to GCTRL in θ (p > 0.05). G2% showed no difference in SFE compared to GCTRL (p > 0.05). The groups with PHMGH presented antibacterial activity against biofilm and planktonic bacteria, with higher antibacterial activity for higher PHMGH incorporation (p < 0.05). PHMGH provided antibacterial activity for all resin sealant groups and the addition up to 1 wt.% showed reliable physico-chemical properties, maintaining the caries-protective effect of the resin sealant over time.

Abstract This in situ study aimed to evaluate the antibacterial and anti-demineralization effects of an experimental orthodontic adhesive containing triazine and niobium phosphate bioglass (TAT) around brackets bonded to enamel surfaces. Sixteen volunteers were selected to use intra-oral devices with six metallic brackets bonded to enamel blocks. The experimental orthodontic adhesives were composed by 75% BisGMA and 25% TEGDMA containing 0% TAT and 20% TAT. Transbond XT adhesive (TXT) was used as a control group. Ten volunteers, mean age of 29 years, were included in the study. The six blocks of each volunteer were detached from the appliance after 7 and 14 days to evaluate mineral loss and bacterial growth including total bacteria, total Streptococci, Streptococci mutans, and Lactobacilli. Statistical analysis was performed using GLM model - univariate analysis of variance for microhardness and 2-way ANOVA for bacterial growth (p<0.05). The 20% TAT adhesive caused no difference between distances from bracket and the sound zone at 10-µm deep after 7 and 14 days. After 14 days, higher mineral loss was shown around brackets at 10- to 30-µm deep for TXT and 0% TAT adhesives compared to 20% TAT. S. mutans growth was inhibited by 20% TAT adhesive at 14 days. Adhesive with 20% TAT showed lower S. mutans and total Streptococci growth than 0% TAT and TXT adhesives. The findings of this study show that the adhesive incorporated by triazine and niobium phosphate bioglass had an anti-demineralization effect while inhibiting S. mutans and total Streptococci growth. The use of this product may inhibit mineral loss of enamel, preventing the formation of white spot lesions.

RESUMO Objetivo: Comparar o desempenho de dois sistemas rotatórios em relação ao tempo de preparo, formato final e alterações do canal, desvio e fratura de instrumento. Métodos: Um total de 40 canais simulados em blocos de resina com curvatura de 30o e comprimento de 17 mm foram divididos randomicamente nos sistemas ProTaper e BioRaCe preparados até F5 e BR5 respectivamente. Imagens pré e após o preparo dos canais foram obtidas e superpostas para identificação de alterações de forma, desvios e largura. O tempo de preparo e fratura de instrumentos também foram avaliados. Os dados foram analisados por teste t de Student. Resultados: O tempo de preparo, alterações de forma e taxa de fratura de instrumentos não teve diferença entre os dois sistemas avaliados (p>0,05). Os instrumentos progressivos do ProTaper resultou em canais significativamente mais largos no terço apical (p<0,05). Conclusão: Os dois sistemas rotatórios avaliados resultaram em preparo endodôntico seguro, com poucas alterações e fratura de instrumento.

ABSTRACT Objective: The aim of this study was to compare the performance of two nickel-titanium rotary systems regarding the preparation time, final shape of canal, incidence of aberration, transportation, and fracture of instrument. Methods: A total of 40 simulated canals in resin blocks with 30o curves and a length of 17 mm were divided randomly into two groups: preparation with ProTaper and BioRaCe systems up to F5 and BR5 respectively. Pre- and post-operative canal images were taken and superimposed in order to identify aberrations, transportation, and to take measurements of the canal width. In addition, the preparation time and instrument fractures were recorded. The data were analyzed using Student's t test. Results: There is no difference (p>.05) comparing the systems regarding preparation time, canal aberration, and instrument fracture rates. The progressive tapered instruments of ProTaper prepared significantly larger canal widths in the apical third (p<.05). Conclusion: Overall, both systems provided safe canal preparation, associated with few canal aberrations and instrument fractures.

Abstract The effects of disinfection by microwave irradiation and immersion in peracetic acid on the physical-mechanical properties of a microwave-activated acrylic resin were evaluated. Specimens of acrylic resin were divided into a control group (specimens not disinfected) and 2 test groups subjected to one disinfection method: microwave irradiation at 850 W for 1 minute or immersion in 50 mL of 0.2% peracetic acid for 5 minutes. Specimens were submitted to Knoop hardness, flexural strength, flexural modulus, Izod impact, water sorption and solubility, glass transition temperature, and degree of conversion tests. Microwave disinfection significantly increased the mean Knoop hardness, Izod impact strength, water sorption, water solubility and glass transition temperature, whereas the flexural properties remained unaffected. Microwave disinfection increased the degree of conversion. Peracetic acid disinfection showed no changes in any properties. Both disinfection techniques did not adversely affect the evaluated properties.

Abstract This study aimed to evaluate the in situ degree of conversion, contact angle, and immediate and long-term bond strengths of a commercial primer and an experimental adhesive containing indomethacin- and triclosan-loaded nanocapsules (NCs). The indomethacin- and triclosan-loaded NCs, which promote anti-inflammatory and antibacterial effects through controlled release, were incorporated into the primer at a concentration of 2% and in the adhesive at concentrations of 1, 2, 5, and 10%. The in situ degree of conversion (DC, n=3) was evaluated by micro-Raman spectroscopy. The contact angle of the primer and adhesive on the dentin surface (n = 3) was determined by an optical tensiometer. For the microtensile bond strength µTBS test (12 teeth per group), stick-shaped specimens were tested under tensile stress immediately after preparation and after storage in water for 1 year. The data were analyzed using two-way ANOVA, three-way ANOVA and Tukey’s post hoc tests with α=0.05. The use of the NC-loaded adhesive resulted in a higher in situ degree of conversion. The DC values varied from 75.07 ± 8.83% to 96.18 ± 0.87%. The use of NCs in only the adhesive up to a concentration of 5% had no influence on the bond strength. The contact angle of the primer remained the same with and without NCs. The use of both the primer and adhesive with NCs (for all concentrations) resulted in a higher contact angle of the adhesive. The longitudinal μTBS was inversely proportional to the concentration of NCs in the adhesive system, exhibiting decreasing values for the groups with primer containing NCs and adhesives with increasing concentrations of NCs. Adhesives containing up to 5% of nanocapsules and primer with no NCs maintained the in situ degree of conversion, contact angle, and immediate and long-term bond strengths. Therefore, the NC-loaded adhesive can be an alternative method for combining the bond performance and therapeutic effects. The use of an adhesive with up to 5% nanocapsules containing indomethacin and triclosan and a primer with no nanocapsules maintained the long-term bond performance.

Resumo O objetivo desse estudo foi desenvolver e avaliar a adição de 1,3,5-triacryloylhexahydro-1,3,5-triazine a uma resina adesiva experimental em diferentes concentrações. Resinas adesivas experimentais foram obtidas a partir da mistura de 50% em peso de bisphenol A glycol dimethacrylate (BisGMA), 25% em peso de triethylene glycol dimethacrylate (TEGDMA), 25% em peso de hidroxietil metacrilato (HEMA) e sistema fotoiniciador. O composto de triazina foi adicionado em proporções de 1; 2,5 e 5% em peso a resina adesiva base e um grupo permaneceu sem a adição do composto de triazina como grupo controle. As resinas adesivas experimentais foram analisadas por atividade antibacteriana (n=3), grau de conversão (n=3) e degradação em solvente (n=3). A distribuição dos dados foi avaliada por teste de Kolmogorov-Smirnov, teste t pareado, ANOVA de uma via e Tukey, considerando nível de significância de 5%. Todos os grupos com adição de composto de triazina demonstraram atividade antibacteriana contra Streptococcus mutans (p<0,05). Todos os grupos atingiram mais de 70% de grau de conversão, mas não houve diferença estatística para essa propriedade química (p>0,05). A dureza Knoop inicial foi maior para os grupos com 2,5 e 5% de triazina (p<0,05) e ambos os grupos apresentaram menor variação percentual de dureza Knoop após degradação em solvente. No presente estudo, foi produzida uma resina adesiva antibacteriana com agente sem liberação para o meio, capaz de copolimerizar com a blenda comonomérica, melhorando as propriedades do material restaurador.

Abstract The aim of this study was to formulate and evaluate an experimental adhesive resin with the addition of 1,3,5-triacryloylhexahydro-1,3,5-triazine at different concentrations. Experimental adhesive resins were obtained by mixing 50% wt bisphenol A glycol dimethacrylate (BisGMA), 25% wt triethylene glycol dimethacrylate (TEGDMA), 25% wt 2-hydroxyethyl methacrylate (HEMA) and photoinitiator system. The triazine compound was added in 1, 2.5 and 5% wt to a base adhesive resin and one group remained with no triazine as control group. The experimental adhesive resins were analyzed for antibacterial activity (n=3), degree of conversion (n=3) and softening in solvent (n=3). Data distribution was evaluated by Kolmogorov-Smirnov test, paired t test, one-way ANOVA and Tukey’s with a 0.05 level of significance. All groups with added triazine compound showed antibacterial activity against Streptococcus mutans (p<0.05). All groups achieved more than 70% degree of conversion, but there was no difference in this chemical property (p>0.05). The initial Knoop hardness was higher in 2.5 and 5% wt groups (p<0.05) and both groups present lower percentage variation of Knoop hardness after solvent degradation. The present study formulated an antibacterial adhesive resin with a non-releasing agent able to copolymerize with the comonomeric blend, improving the restorative material’s properties.

RESUMO Objetivo: Analisar se corantes e fibras de nylon influenciam nas propriedades de uma resina acrílica ativada por energia de micro-ondas. Métodos: Espécimes retangulares e em forma de disco foram confeccionados em resina acrílica rosa médio com e sem fibras de nylon e incolor sem fibras. Para obter os espécimes retangulares, foi utilizada uma matriz de aço inoxidável com as seguintes dimensões: 64 X 10 X 3 (± 0,5mm) e para obter os espécimes em forma de disco, foi utilizada uma matriz com 50mm (± 0,5mm) de diâmetro e 0,5mm (±0,05mm) de espessura. Os mesmos foram randomizados para formar os grupos controle (acrílico incolor sem fibras) e experimentais (rosa médio com e sem fibras), sendo cada grupo composto por dez (10) espécimes retangulares e cinco (5) em forma de disco. Foram os mesmos então submetidos a seis (6) ensaios (resistência ao impacto izod, n=10; dureza knoop, n=10; temperatura de transição vítrea, n=3; sorção e solubilidade, n=5; grau de conversão, n=1; resistência à flexão e módulo de flexão, n=10). Todas as variáveis foram submetidas à análise de variância seguida pelo teste de comparações múltiplas de Tukey, com nível de significância de 5%. Resultados: O grau de conversão foi de 88% para os 3 grupos de resinas e os resultados não mostraram diferença estatisticamente significativa entre os mesmos para cada variável (p>0,05). Conclusão: Os resultados mostraram que o corante e a presença de fibras de nylon em resina acrílica não afetaram as propriedades analisadas nesse estudo.

ABSTRACT Objective: The aim of this study is to analyze if both color and nylon fibers have an influence on microwave-cured acrylic resin properties. Methods: Rectangular and disk-shaped specimens were prepared using acrylic resins; medium pink with and without nylon fibers and colorless without nylon fibers. To obtain the rectangular specimens, a stainless steel die was used with the following dimensions: 64 X 10 x 3 mm (± 0.5mm). To obtain disk-shaped specimens, a die 50mm (±0.5mm) in diameter and 0.5mm (±0.05mm) thick was employed. They were randomized to form groups: control (colorless acrylic) and experimental (medium pink, with and without nylon fibers), with each group consisting of ten (10) specimens rectangular in shape and five (5) disk-shaped. They were analyzed in six (6) assays (izod impact strength, n=10; Knoop hardness, n=10; glass transition temperature, n=3; water sorption and solubility, n=5; degree of monomer/polymer conversion, n=1; flexural strength and flexural modulus, n=10). All variables were subjected to the analysis of variance test followed by Tukey's multiple comparison test, at a 5% level of significance. Results: The analysis of the monomer/polymer degree of conversion did not reveal any difference between the three groups of resins (medium pink, with and without nylon fibers and colorless resin); it was approximately 88%. The results did not show significant differences between the groups for each variable (p>0.05). Conclusion: The results showed that color and presence of nylon fibers in acrylic resins did not affect the properties analyzed in this study.

Abstract The present study aimed to evaluate effects of different surface treatments and aging of composite cylinders on bond strength of composite resin repair. Thirty-two composite cylinders were produced and divided into four groups according to type of surface treatment and storage time of composite cylinder and repair. Cylinder surface of control group (Gcontrol) received no treatment before composite repair. Other groups were sandblasted with aluminum oxide (GAl2O3), followed by silane (GAl2O3sil) or adhesive (GAl2O3ad). Composite cylinders were stored in artificial saliva for either 24 hours or 1 year. Repairs were performed and stored in artificial saliva for 24 hours or 1 year and repair strength was evaluated using microtensile bond strength test. Data were submitted to Student’s t test, two-way ANOVA, and post hoc test for storage time and treatment (α = 0.05). Gcontrol group showed lower values of aging of composite cylinder and storage time of repair (24 hours or 1 year for both) compared with other groups (p < 0.05). GAl2O3ad and GAl2O3sil groups did not exhibit decreased microtensile bond strength with aged repairs (1 year; p > 0.05). Polymer degradation was significant for composite cylinders during the first year of storage in Gcontrol, GAl2O3, and GAl2O3ad groups (p < 0.05). In GAl2O3sil group, storage time of composite cylinders was not significant (p > 0.05). Aging of composite resin influenced bond strength of restoration repair for up to 1 year. Sandblasting with Al2O3, followed by application of silane layer, produced high bond strength after composite or repair aging.